Electrochemical Device With A LSGM-Electrolyte

ABSTRACT

An electrochemical device including an anode, a cathode and an electrolyte membrane disposed between the anode and the cathode, wherein the electrolyte membrane has a material of formula La 1−x Sr x Ga 1−y MG y O 3−0.5(x+y) , wherein x and y are independently a value of 0.1 to 0.3, said material having a relative density of at least 90% and including LaSrGaO 4  in a percentage of 0.05 vol % to 10 vol %. A method for producing energy and a method for separating oxygen from a gas mixture are also disclosed.

BACKGROUND OF THE INVENTION

The present invention relates to an electrochemical device, and more particularly a solid state electrochemical device composed of electrodes in contact with a solid state electrolyte membrane.

PRIOR ART

The active basic structure of an electrochemical device such as a solid oxide fuel cell (SOFC) or a gas separator/generator (e.g. oxygen generator) consists of an electrolyte layer (electrolyte membrane) interposed between an anode and a cathode. Typically, electrolyte membrane, cathode and anode contain ceramics and/or cermets.

In the solid oxide fuel cell, the cathode is supplied with oxygen (for example air) and the anode is supplied with a fuel gas (H₂, CO, or other gas). The cathode and the anode are porous so that the gas reaches the interface with the solid electrolyte membrane, which is composed by a material capable of conducting ionic species. Oxygen supplied to the cathode moves to the interface with the solid electrolyte through the pores in the cathode, there receives electrons from the anode and is ionized to oxide ions (O²⁻). The oxide ions move toward the anode by diffusing through the solid electrolyte layer, and, close to the interface with the anode, react with the fuel gas creating reaction products (e.g. H₂O, CO₂), and releasing electrons from the anode.

Generally, electrochemical devices use yttria-stabilized zirconia (YSZ) as the electrolyte membrane. This requires an operating temperature of about 1000° C. The material interconnecting individual cells has to be stable in the oxidizing atmosphere at the cathode, in the reducing atmosphere at the anode, and at an operating temperature of about 1000° C. This implies the use of special materials, such as a conducting ceramic, for the interconnection.

An operating temperature in the range of 600°-800° C. could allow the use of an oxidation resistant stainless steel or other alloys as the interconnect material. The lower operating temperature would also reduce operating costs, increase durability, extend life service, and permit more frequent cycling.

One of the approaches to an operating temperature lower than 800° C. is the use of a solid electrolyte having an oxide-ion conductivity at or below such temperature that is comparable to that of YSZ at 1000° C. The most promising material for such approach is CeO₂ (ceria) doped with an alkaline-earth oxide or a rare earth oxide, but reduction of Ce⁴⁺ to Ce³⁺ in the anodic gas introduces into the electrolyte an undesired parasitic electronic leak conduction.

There is a need for a solid electrolyte having a high oxide-ion conductivity at a reduced operating temperature, negligible electronic conductivity over a wide range of oxygen partial pressure, e.g. 10⁻²²<Po₂<1 atm, and stable performance over extended periods of time.

The perovskite system La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y)) (hereinafter referred to as “doped gallate” or “LSGM”) wherein x and y are of from 0.1 to 0.3 is attracting increasing attention as an oxide-ion solid electrolyte competitive with yttria-stabilized zirconia; it demonstrates an oxide-ion conductivity σ₀=0.10 S/cm at 800° C., a negligible electronic conduction at temperatures T<1000° C. over a broad range of oxygen partial pressure from pure oxygen Po₂=1 atm) to moistened hydrogen (Po₂˜10⁻²² atm), and a stable performance over long operating periods. These superior electrical and chemical properties make it a candidate for use as the solid electrolyte in reduced-temperature electrochemical devices operating at or below 800° C.

LSGM electrolyte membranes are known, e.g. from U.S. Pat. No. 6,004,688. This patent document teaches the necessity of using a phase pure LSGM. At room temperature LSGM contains an undesirable non-conducting phase LaSrGaO₄ (also known as 214) which may cause the decrease of ionic conductivity of the electrolyte membrane.

Moreover, U.S. Pat. No. 6,004,688 reports that a reaction occurs between LSGM and nickel (Ni), which is often used as anode material. Such reaction brings to the formation of the metallic perovskite LaNiO₃, which is a poor oxide-ion conductor and may cause an undesired anode overpotential. In order to avoid the formation of LaNiO₃, U.S. Pat. No. 6,004,688 provides a buffer layer of, e.g., samaria- or gadolinia-doped ceria, between the anode and the electrolyte layer, so as to block the unwanted chemical reaction without suppressing the oxide-ion permeability.

P. Majewski et al., J. Electroceramics, 8(1), 65-73, 2002 relates to various methods for preparing, inter alia, La_(0.8)Sr_(0.2)Ga_(0.8)Mg_(0.2)O_(3−x) with a particular focus on density and phase purity. The so-called mixed oxide route yields a LSGM single phase with a density of 90% (measured by the Archimedes method) after treating at 1400° C. for about 60 hours. At temperatures of 1400° C., the combustion synthesis yields LSGM powders containing about 5 vol % of LaSrGa₃O₇ phase (another secondary, non-conducting phase also known as 237), while the Pechini method, even after calcinations at 1400° C. for 6 hours, yields LSGM powders still no single-phase and containing about 5 vol % of the phases LaSrGa₃O₇ and LaSrGaO₄, and with a density of 85%.

K. Huang and J. B. Goodenough, Journal of Alloys and Compounds, 303-304 (2000), 454-464 relates to a Sr- and Mg-doped LaGaO₃ (LSGM) with a LaSrGaO₄ phase impurity. Also this paper teaches the necessity of an interfacial layer between anode and electrolyte membrane for avoiding reactions occurring between Ni and LSGM.

Problem Underlying the Invention

The Applicant faced the problem of having an electrochemical device operating at low temperatures. The use of an electrolyte membrane comprising LSGM involves various problems.

A phase pure LSGM with a high density is difficult to obtain by industrially feasible methods. The high density is desirable because it helps the mechanical strength and provides the electrolyte membrane with gas-tight feature. The presence of secondary non-conducting phases impairs the performance of the LSGM-based electrolyte membrane.

The Applicant perceived that a controlled amount of the LaSrGaO₄ phase in an electrolyte membrane comprising LSGM having a high density was satisfactory for the performance of the electrochemical device, in particular in term of conductivity.

The flexibility in the choice of the anode material was another issue to the Applicant. Especially, the use of nickel is attractive because of its high catalytic activity for the anode reaction and its relatively low cost, but its reactivity with LSGM demands to employ an interlayer between the anode and the electrolyte membrane.

Applicant surprisingly observed that in an electrochemical device comprising an anode containing nickel and an electrolyte membrane containing high density LSGM together with a controlled amount of LaSrGaO₄, formation of by-product LaNiO₃ is substantially avoided.

SUMMARY OF THE INVENTION

Therefore, the present invention relates to an electrochemical device comprising an anode, a cathode and an electrolyte membrane disposed between said anode and said cathode, wherein said electrolyte membrane comprises a material of formula

La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y))

wherein x and y are independently a value of from 0.1 to 0.3, extremes included, said material having a relative density of at least 90% and comprising LaSrGaO₄ in a percentage of from 0.05 vol % to 10 vol %, extremes included.

Examples of electrochemical devices according to the present invention are solid oxide fuel cells (SOFCs), molten carbonate fuel cells (MCFCs), gas separators and gas sensors.

Preferably, the anode and cathode of the electrochemical device of the invention show a porosity of at least 10%, more preferably of at least 30%.

In a first preferred embodiment, the anode of the electrochemical device of the present invention comprises a cermet wherein the metallic portion is an alloy including nickel and at least a second metal selected from aluminium, titanium, molybdenum, cobalt, iron, chrome, copper, silicon, tungsten and niobium, and the ceramic portion is selected from doped ceria and La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y)) wherein x and y are as above. Reference is made to WO04/038844 in the Applicant's name.

Preferably, said alloy has an average particle size not higher than 20 nm, more preferably not higher than 16 nm.

Advantageously, the alloy shows a mean surface area higher than 20 m²/g, preferably higher than 30 m²/g, and more preferably higher than 40 m²/g.

Preferably the alloy has a second metal content of from about 1% by weight to about 99% by weight, more preferably, and even more preferably from about 40% by weight to about 60% by weight. Advantageously, said second metal is copper.

Preferably the alloy has a nickel content of from about 1% by weight to about 99% by weight, more preferably from about 30% by weight to about 70% by weight, and even more preferably of about 50% by weight.

The ceramic portion of said cermet advantageously shows a particle size not higher than 50 nm, preferably from about 1 to about 25 nm.

Preferably, the ceramic portion is doped ceria selected from gadolinia-doped ceria (CGO) and samaria-doped ceria (SDC).

Optionally, the anode of the first embodiment of the invention comprises cerium oxide (CeO₂), optionally added with additives like cobalt.

Advantageously, the electrochemical device of the invention comprises and anode containing nickel and an electrolyte membrane comprising a material of formula La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y)) wherein x and y are independently a value of from 0.1 to 0.3, extremes included, said material having a relative density of at least 90% and comprising LaSrGaO₄ in a percentage of from 0.05 vol % to 10 vol %, extremes included, said electrolyte membrane being in direct contact with at least said anode, i.e. no additional layers are interposed between the anode and the electrolyte membrane.

In a second embodiment, the anode of the electrochemical device of the invention comprises a ceramic containing at least one of cobalt and iron, said ceramic being mixed with doped ceria.

Preferably, the ratio ceramic/doped ceria is of from about 50:50 to about 95:5, more preferably from about 60:40 to about 80:20.

Preferably said ceramic has a perovskite structure or a perovskite-related structure. The term “perovskite” and “perovskite-related” refer to a class of materials comprising a structure based upon the structure of the mineral perovskite, CaTiO₃. In its idealized form, the perovskite structure has a cubic lattice in which a unit cell contains metal ions at the corners of the cell, another metal ion in its center and oxygen ions at the midpoints of the cube's edges. This is referred to as an ABO₃-type structure, in which A and B represent metal ions.

Preferably said ceramic contains cobalt and iron.

Examples of said ceramic have a formula

-   -   M_(2−z)Sr_(z)Fe_(2−w)Co_(w)O_(5±δ) wherein M is Ca or a rare         earth element; z and w are independently a value of from 0 to 2,         extremes included, and δ is from stoichiometry; or     -   M_(a)Sr_(1−a)Fe_(1.5−b)Co_(b)O_(3+δ) wherein M is Ca or a rare         earth element; wherein a and b are independently a value of from         0 to 0.7, extremes included, and δ is from stoichiometry.

For example, the ceramic of the anode of the second embodiment is La_(0.8)Sr_(0.2)FeO₃.

Also, a ceramic for the anode of the second embodiment of the invention can be a lanthanum strontium cobalt iron oxide having, for example, a general formula La_(1−c)Sr_(c)Co_(1−d)Fe_(d)O_(3−δ), wherein c and d are independently a value of from 0 to 1, extremes included, and δ is from stoichiometry. Preferred is a lanthanum strontium cobalt iron oxide of formula La_(0.6)Sr_(0.4)Co_(0.2)Fe_(0.8)O_(3−δ) (hereinafter referred to as LSCF-80).

Preferably, the anode of the second embodiment of the invention is metal-free. With metal-free it is intended that none of the elements present in the anode is in a metallic form.

The doped ceria of the second embodiment can be selected from the same of the same class of materials defined above for the first embodiment.

A first type of cathode for the electrochemical device of the invention can comprise a metal such as platinum, silver or gold or mixtures thereof, and an oxide of a rare earth element, such as praseodymium oxide.

A second type of cathode can comprise a ceramic selected from

-   -   La_(1−e)Sr_(e)Mn_(f)O_(3−δ), wherein e and f are independently a         value of from 0 to 1, extremes included, and δ is from         stoichiometry; and     -   La_(1−c)Sr_(c)Co_(1−d)Fe_(d)O_(3−δ), wherein c, d and δ are as         above.

Said second type of cathode can further comprise a doped ceria.

A third type of cathode can comprise materials above mentioned for the cathodes of the first and second type.

Preferably, the electrolyte membrane material of formula La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y)) has a perovskite structure.

Preferably said material is of formula La_(0.8)Sr_(0.2)Ga_(0.8)Mg_(0.2)O_(3−δ).

Advantageously said material has a relative density of from about 95% to about 99%, extremes included.

Preferably, LaSrGaO₄ is present in a percentage of from 0.1 vol % to 6 vol %, extremes included.

Advantageously LaSrGaO₄ is present in an amount increasing from the surface to the interior of the electrolyte membrane. Preferably, the amount of LaSrGaO₄ at the surface of the electrolyte membrane is substantially null.

Advantageously, the electrolyte membrane material of formula

La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y))

is substantially free from LaSrGa3O₇. As “substantially free” it is intended that the percentage of LaSrGa3O₇ is lower than 2 vol %. The anode, the cathode and the electrolyte membrane of the electrochemical device of the invention can be prepared by known methods.

Preferably, at least the electrolyte membrane is produced by performing at least the following steps of

-   -   thermally treating an aqueous solution comprising metal cations,         at least one hydrosoluble ethylenically unsaturated monomer with         an ester moiety, and a hydrosoluble cross-linking monomer with         at least two ethylenically unsaturated ester moieties, to         provide a gel and to obtain said metal cations in an oxide form;     -   calcining said gel to remove organic substances and to form a         crystal phase of said metal oxides in nanosize powder form;     -   sintering said powder to provide the ceramic material.

As aqueous solution is intended a solution wherein as solvent water or a mixture of water and at least one hydrosoluble solvent is used. As hydrosoluble solvent an alcohol, glycol, tetrahydrofurane, dioxane may be used.

The metal cations solution can be obtained by dissolving hydrosoluble precursors thereof. Examples of precursors are oxides, chlorides, carbonates, β-diketonates, hydroxides, nitrates, acetates, oxalates, and mixtures thereof.

Advantageously, the concentration of each of the metal cations in the aqueous solution is higher than 0.5 mol/l, preferably from 1 to 10 mol/l.

Preferably, hydrosoluble ethylenically unsaturated monomers with an ester moiety used for producing the electrochemical device of the present invention

are encompassed by the general formula (I) wherein R is hydrogen, (C₁-C₄)alkyl, aryl or aryl(C1-C4)alkyl; R₁ is a C₁-C₈ hydrocarbon group containing at least one polar group selected from —COOH, —NH₂, —NHR′, —N(R′)₂, —OH, —OR′—SO₃H, —SH, wherein R′ is a (C₁-C₆)alkyl group; and R₂ is hydrogen, methyl, ethyl, propyl or phenyl.

Preferably R′ is a (C₁-C₄)alkyl group.

Examples of monomers of formula (I) are (meth)acrylate monomers such as 2-hydroxyethyl acrylate, 2-hydroxypropyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate, 2-hydroxyethyl phenacrylate, hydroxybutyl acrylate, hydroxybutyl methacrylate, butandiol monoacrylate, 2-(2-ethoxyethoxy)ethyl acrylate, dimethylamino ethyl acrylate, and dimethylamino ethyl methacrylate.

Cross-linking monomers useful for producing the electrochemical device of the invention are preferably selected from diacrylates and triacrylates wherein the acrylates groups are linked to alkoxylated moieties or polyoxyalkylene linear units. Examples are polyethylene glycol, dimethacrylate, ethoxylated trimethylolpropane triacrylate.

Advantageously, said aqueous solution comprises a hydrosoluble polymerization initiator, such as α,α′-azaisobutyronitrile (AIBN), tetramethylene-ethylenediamine, peroxides, e.g. hydrogen peroxide, benzoyl peroxide or dicumyl peroxide, persalts, e.g. ammonium, sodium or potassium persulfate.

Preferably, the aqueous solution is thermally treated at a temperature ranging between about 50° C. and about 150° C.

By the term “gel” as used throughout the specification and claims, it is intended a jellylike, non-flowable structure based on a polymeric network entrapping a liquid phase comprising solvent, reactants and not cross-linked polymer chains.

Before proceeding to the calcining step, the gel obtained by the process of the invention is optionally dried to obtain a xerogel.

Said xerogel is a substantially dry, hard gel resulting from the removal of the aqueous phase from the gel, which usually causes a shrinkage of the gel network.

This optional drying step is preferably carried out by heating at a temperature ranging between about 80° C. and about 300° C.

Advantageously, the xerogel is disaggregated by known techniques, e.g. grinding or ball-milling, and subjected to the calcining step.

The calcining step is preferably carried out at a temperature ranging between about 300° C. and about 1500° C. This treatment results in the removal of residual impurities such as solvent and organic substances, and the crystallization of the oxide or mixed oxide phase in form of a nanosize powder.

In an embodiment of the invention, the calcining step is carried out by progressively increasing temperature. This is preferable when the temperature for eliminating the impurities is different, and it is typically lower, than the crystallization temperature. Advantageously, at least one grinding step of the powder is carried out at an intermediate stage of the calcining step.

As “nanosize powder” it is intended a powder having a mean primary grain size lower than 1,000 nm, preferably lower than 100 nm. Advantageously, the nanosize powders obtained by the process of the invention show a mean primary grain size lower than 20 nm, for example comprised between about 3 nm and 15 nm.

By the term “primary grain size” as used throughout the specification and claims, it is intended the size of the primary particles which are distinguishable units in a transmission electron micrograph (TEM).

Advantageously, before the sintering step the nanosize powder is treated at a temperature of 700° C.-1100° C.

Advantageously, before the sintering step the nanosize powder is compacted in pellets or shaped in form of electrolyte membrane for the electrochemical device of the invention.

Advantageously, the ceramic material is obtained already in the shape suitable for the electrolyte membrane of the electrochemical device of the invention.

Alternatively, at least the electrolyte membrane of the electrochemical device of the invention can be prepared according to A. Sin and P. Odier, Advanced Materials, Vol. 12, No. 9 (2000)649-652.

In a further aspect, the present invention relates to a method for producing energy comprising the steps of:

-   -   feeding at least one fuel into an anode side of a solid oxide         fuel cell comprising an anode, a cathode and an electrolyte         membrane disposed between said anode and said cathode, wherein         said electrolyte membrane comprises a material of formula         La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y)) wherein x and y are         independently a value of from 0.1 to 0.3, extremes included,         said material having a relative density of at least 90% and         comprising LaSrGaO₄ in a percentage of from 0.05 vol % to 10 vol         %, extremes included;     -   feeding an oxidant into a cathode side of said solid oxide fuel         cell; and     -   oxidizing said at least one fuel in said solid oxide fuel cell,         resulting in production of energy.

A fuel suitable for the method of the present invention can be selected from hydrogen; an alcohol such as methanol, ethanol, propanol; a hydrocarbon in gaseous form such as methane, ethane, butene; carbon dioxide, carbon monoxide, natural gas, reformed natural gas, biogas, syngas and mixture thereof, in the presence of water (steam fuel); or an hydrocarbon in liquid form, e.g. diesel, toluene, kerosene, jet fuels (JP4, JP-5, JP-8, etc). Preferably the fuel is methane.

Advantageously, the hydrocarbon fuel is substantially dry. As “substantially dry” it is intended that the water content can be lower than 10 vol %. The substantially dry fuel is directly oxidized at the anode side. Preferred for the present invention is substantially dry methane.

Advantageously, the solid oxide fuel cell employed by the method of the invention operates at a temperature ranging between about 400° C. and about 800° C., more preferably between about 500° C. and about 700° C.

Besides the possibility of skipping the necessity of using special thermo-resistant material, an advantage provided by low operating temperatures, such those preferred by the present invention, is the reduction of NO_(x) formation at the cathode. The formation of such undesired by-products is due to the reaction of the nitrogen present in the air fed at the cathode side, such reaction being related to temperature increase.

The solid oxide fuel cell according to method of the invention substantially displays a great flexibility in the choice of the fuel to be fed with. Besides hydrocarbons, it can performs by feeding the anode also with hydrogen, or with a wet hydrocarbon fuel (in the case of methane, generally 1:3 methane/water) to provide reformed fuel.

In case of operating with reformed fuel, the fuel can be internally reformed at the anode side.

In another further aspect, the present invention relates to a method for separating oxygen from a gas mixture, comprising the steps of:

-   -   feeding the gas mixture into a cathode side of a gas separator         comprising an anode, a cathode and an electrolyte membrane         disposed between said anode and said cathode, wherein said         electrolyte membrane comprises a material of formula         La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y)) wherein x and y are         independently a value of from 0.1 to 0.3, extremes included,         said material having a relative density of at least 90% and         comprising LaSrGaO₄ in a percentage of from 0.05 vol % to 10 vol         %, extremes included;     -   applying an external potential difference between the cathode         and the anode;     -   dissociating the oxygen at the cathode to yield oxygen ions;     -   diffusing the oxygen ions through the electrolyte membrane from         the cathode to the anode; and     -   converting the diffused oxygen ions to oxygen at the anode.

Preferably, the gas mixture of the above method is air.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention will be further illustrated hereinafter with reference to the following examples and figures, wherein:

FIG. 1 schematically shows an electrochemical device according to the invention;

FIG. 2 shows the X-ray diffraction (XRD) pattern of an anode powder;

FIG. 3 shows surface and internal X-ray diffraction (XRD) patterns of a La_(0.20)Sr_(0.80)Ga_(0.80)Mg_(0.20)O_(2.8) pellet;

FIG. 4 relates to conductivity values of an electrolyte membrane of the electrochemical device according to the invention and one of the prior art;

FIG. 5 show an XRD pattern of LSGM according to the prior art;

FIG. 6 illustrates a comparison of conductivity values with of an electrolyte membrane of the electrochemical device according to the invention and one of the prior art;

FIG. 7 shows the XRD pattern of a, stability study at the anode/electrolyte membrane interface.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

FIG. 1 schematically illustrates an electrochemical device which is a solid oxide fuel cell comprising anode, cathode and electrolyte membrane (indicated as “electrolyte”) with the reactant/product gases and the ion conduction flow directions through the cell. Gaseous fuels, e.g. hydrogen or hydrocarbons, are fed continuously to the anode (negative electrode) and an oxidant (i.e., oxygen from air) is fed continuously to the cathode (positive electrode); the electrochemical reactions take place at the electrodes to produce an electric current.

The architecture of a gas separator is substantially analogous (anode, cathode and electrolyte membrane). Similarly to a fuel cell, air or an oxygen containing gas is provided to the cathode. By an electrical potential applied across an oxygen ion conductive electrolyte membrane via electrodes, oxygen is dissociated and reduced at the cathode. Oxygen ions travel through the electrolyte, and are oxidized and recombined at the anode to produce oxygen.

Example 1 Preparation of Cu_(0.47)Ni_(0.53) and Ce_(0.8)Gd_(0.2)O_(1.9) Cermet

1.164 g of Cu was added with 5 ml of H₂O while stirring and heating up to boiling. HNO₃ (3.5 ml; 63%) was dropwise added. 1.212 g of Ni was then added followed by HNO₃ (63%) up to a total acid volume of 4.3 ml.

The resulting mixture was added with 5.992 g. of Ce(NO₃)₃×6H₂O, 1.370 g of Gd(NO₃)₃×6H₂O and water up to a total volume of 15 ml to provide a solution with a metal cation concentration of 3.747 mol/l.

The resulting mixture was added with 15 ml of 2-hydroxyethylmethacrylate, 7.5 ml of polyethylene glycol dimethacrylate and 100 mg of AIBN, and heated (80° C.) up to the gel formation.

The gel was dried at 200° C. for 2 h to yield a xerogel which was ground, crashed and decomposed at 500° C. for 1 h. A powder mixture (6 g) of CuO, NiO, Cu_(0.47)Ni_(0.53)O and Ce_(0.8)Gd_(0.2)O_(1.9) (hereinafter CGO-20) was obtained and characterized as follows.

FIG. 2 shows the XRD analysis of the powder mixture. The mean primary grain size was calculated from the XRD patterns by use of the Debye-Scherrer formula (A. R. West “Solid State Chemistry and its application” Ed. John Wiley & Sons, 1996, page 174) giving values of 10 nm for NiO (together with the isostructural phase (Ni, Cu)O), 12 nm for CuO and 5 nm for CGO-20. The TEM imaging was in agreement with the calculated mean primary grain size. Moreover, it is not possible to distinguish all phases by shape due to their intimate mixing. The powders were weakly agglomerated as from SEM images.

The powder mixture was reduced at 500° C. for 2 h in H₂ (100%) to give the title cermet. According to the XRD pattern of FIG. 2 the resulting NiCu alloy pure phase has a mean primary grain size of 8 nm, and the CGO-20 has a mean primary grain size of 6 nm.

Example 2 Preparation of La_(0.60)Sr_(0.40)Fe_(0.80)Co_(0.20)O_(3−δ)/Ce_(0.8)Gd_(0.2)O_(1.9) A. Cerium/Gadolinium Oxides Powder and Ce_(0.8)Gd_(0.2)O_(1.9)

-   -   1.8716 g of Ce(NO₃)₃.6H₂O and 0.4279 g of Gd(NO₃)₃.6H₂O were         added to 10 ml of H₂O while stirring and heating up to 50° C.         resulting in a concentration of 0.538 mol/l of H₂O.         Subsequently, 10 ml of 2-hydroxyethylmethacrylate and 5 ml of         poly(ethyleneglycol)diacrylate were added. The solution was         heated up to 100° C. 20 drops of 35% H₂O₂ were added to initiate         the gel formation. The resulting gel was decomposed at 500° C.         for 5 h. 1 g of the title compound was obtained and         characterized as follows.     -   Ce_(0.8)Gd_(0.2)O_(1.9) powder showed an average particle size         of 10 nm calculated using the Debye-Scherrer formula (A. R. West         “Solid State Chemistry and its application” Ed. John Wiley &         Sons, 1996, page 174).

B. La_(0.60)Sr_(0.40)Fe_(0.80)Cu_(0.20)O_(3−δ) Powder

-   -   1.0064 g of La(NO₃)₃.6H₂O, 0.3278 g of Sr(NO₃)₂, 1.2596 g of         Fe(NO₃)₃.9H₂O and 0.2254 g of Co(NO₃)₂.6H₂O were added to 10 ml         of H₂O while stirring and heating up to 50° C. resulting in a         concentration of 0.776 mol/l of H₂O. Subsequently, 10 ml of         2-hydroxyethylmethacrylate and 5 ml         poly-(ethyleneglycol)diacrylate were added. The solution was         heated at 80° C. 20 drops of 35% H₂O₂ were added to initiate the         gel formation. The resulting gel was decomposed at 500° C. for 5         h and at 700° C. for 5 h. 1 g of the title compound were         obtained. The powder showed an average particle size of 10 nm         calculated using the Debye-Scherrer formula (A. R. West “Solid         State Chemistry and its application” Ed. John Wiley & Sons,         1996, page 174).     -   C. 0.35 g of La_(0.60)Sr_(0.40)Fe_(0.80)Co_(0.20)O_(3−δ) (70 wt         %) and 0.15 g of Ce_(0.8)Gd_(0.2)O_(1.9) (30 wt %) were mixed in         agate mortar. Then, 1 ml of isopropyl alcohol was added and the         obtained slurry was treated in ultrasound bath for 1 hour.

Example 3 La_(0.20)Sr_(0.80)Ga_(0.80)Mg_(0.20)O_(2.8) Containing LaSrGaO₄ Phase

1.1086 g of La(NO₃)₃.6H₂O, 0.1641 g of Mg(NO₃)₂.6H₂O, 0.1354 g of Sr(NO₃)₂ and 0.6762 g of Ga(NO₃)₃0.5H₂O were dissolved in 75 ml of H₂O. The solution was heated at 60° C., than 5.6935 g of acrylamide, 0.6328 g of bis-acrylamide and about 15 drops of H₂O₂ are added. The heating temperature was increased, and at 80° C. gel formation began. The gel was dried in microwave oven for some minutes. A xerogel was obtained and crashed and decomposed at 500° C. for 2 hours. The resulting powder was treated at 1450° C. for 5 hours.

The powder showed an average particle size of 40 nm calculated using the Debye-Scherrer formula (A. R. West “Solid State Chemistry and its application” Ed. John Wiley & Sons, 1996, page 174).

FIG. 3 illustrates two XRD patterns of a pellet prepared at 1450° C. for 5 hours with said powder. The surface XRD pattern shows no trace of the LaSrGaO₄ phase (therein marked as 214), whereas this phase is detected inside the pellet.

La_(0.20)Sr_(0.80)Ga_(0.80)Mg_(0.20)O_(2.8) showed a relative density of 98% measured by the Archimedes method with water as the displacement liquid (PSS model apparatus, Gibertini, Italy). A content of LaSrGaO₄ of 3 vol % was calculated from the XRD pattern as the percentage ratio between the intensity of the main peak of LaSrGaO₄ and the intensity of the main peak of LSGM.

Example 4 Electrochemical Device Assembly

The electrolyte membrane was prepared in pellet form according to Example 3. The pellet was prepared from 0.25 g in a cylindrical shape with 13 mm of diameter and a thickness of 200 μm. Onto one side, a layer of slurry of La_(0.60)Sr_(0.40)Fe_(0.80)CO_(0.20)O_(3−δ)/Ce_(0.8)Gd_(0.20)O_(1.9) in isopropyl alcohol (as from Example 2) was painted and thermally treated in air at 1100° C. for 2 hours to obtain the cathode. A layer of Cu_(0.47)Ni_(0.53) and Ce_(0.8)Gd_(0.20)O_(1.9) slurry in isopropyl alcohol (as from Example 1) was painted onto the other side and thermally treated in air at 1100° C. for 2 hours to obtain the anode.

Example 5 Conductivity Tests

The tests were carried out in the temperature range of 400-800° C. using impedance spectroscopy method by a frequency response analyzer Solartron 1255A over a frequency range of 10 Hz-1 MHz. Pt films, obtained from Engelhard-Clal Pt paste, were deposited onto both sides of the electrolyte membrane as electrical contacts and then were treated at 800° C. for 2 h.

FIG. 4 shows an Arrhenius plot obtained from conductivity values of an electrolyte membrane as from Example 4 compared with that of K. Huang and J. B. Goodenough, Journal of Alloys and Compounds, 303-304 (2000), 454-464 which was prepared by repeating the teachings of this paper and was found to have a relative density of 80% and to contain LaSrGaO₄ (214) in an amount of 3.9 vol % and LaSrGa3O₇ (237) in an amount of 14.4 vol %, as from the XRD pattern of FIG. 5. Another test was carried out as the previously described one. The conductivity of the electrolyte membrane obtained as from Example 4 was compared with that disclosed by U.S. Pat. No. 6,004,688. FIG. 6 reports the comparison of conductivity values at 700° C. and 800° C. The conductivity of the electrolyte membrane of the invention is higher.

Example 6 Stability Test at the Anode/Electrolyte Membrane Interface

The possible formation of LaNiO₃ phase at the anode/electrolyte membrane interface was monitored. As already discussed above, such a phase represents an insulating layer between anode and electrolyte membrane thus impairing the electrochemical device performance. On an electrolyte membrane layer as from Example 3 a NiO layer was painted, and the whole was treated at 1100° C. for 2 h. The presence of LaNiO₃ phase provides a peak at 2θ32.92° in the XRD, as illustrated by Zhang et al., Solid State Ionics 133 (2000), 153-160. After the treatment at 1100° C., such a peak was not detectable. The anode/electrolyte membrane assembly was further treated at 1200° C. for 2 h. After the treatment at 1200° C., such a peak was not detectable as from the XRD pattern of FIG. 7. Also, SEM/EDX showed that there is no migration of Ni to the electrolyte and also there is no La in the anodic side that can form the LaNiO₃.

In the electrochemical device of the invention the electrolyte membrane containing LSGM is in direct contact with an anode containing nickel without the formation of the non-conductive phase LaNiO₃. 

1-46. (canceled)
 47. An electrochemical device comprising an anode, a cathode and an electrolyte membrane disposed between said anode and said cathode, wherein said electrolyte membrane comprises a material of formula La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y)) wherein x and y are independently a value of 0.1 to 0.3, said material having a relative density of at least 90% and comprising LaSrGaO₄ in a percentage of 0.05 vol % to 10 vol %.
 48. The electrochemical device according to claim 47, comprising a solid oxide fuel cell, a molten carbonate fuel cell, a gas separator or a gas sensor.
 49. The electrochemical device according to claim 47, wherein the anode and the cathode have a porosity of at least 10%.
 50. The electrochemical device according to claim 49, wherein the anode and the cathode have a porosity of at least 30%.
 51. The electrochemical device according to claim 47, wherein the anode comprises a cermet wherein the metallic portion is an alloy comprising nickel and at least a second metal selected from aluminium, titanium, molybdenum, cobalt, iron, chrome, copper, silicon, tungsten and niobium, and the ceramic portion is selected from doped ceria and La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y)) wherein x and y are as in claim
 47. 52. The electrochemical device according to claim 51, wherein said alloy has an average particle size not higher than 20 nm.
 53. The electrochemical device according to claim 52, wherein said alloy has an average particle size not higher than 16 nm.
 54. The electrochemical device according to claim 51, wherein said alloy has a mean surface area higher than 20 m²/g.
 55. The electrochemical device according to claim 54, wherein said alloy has a mean surface area higher than 30 m²/g.
 56. The electrochemical device according to claim 55, wherein said alloy has a mean surface area higher than 40 m²/g.
 57. The electrochemical device according to claim 51, wherein said alloy has a second metal content of about 1% by weight to about 99% by weight.
 58. The electrochemical device according to claim 57, wherein said alloy has a second metal content of about 40% by weight to about 60% by weight.
 59. The electrochemical device according to claim 51, wherein said second metal is copper.
 60. The electrochemical device according to claim 51, wherein said alloy has a nickel content of about 1% by weight to about 99% by weight.
 61. The electrochemical device according to claim 60, wherein said alloy has a nickel content of about 30% by weight to about 70% by weight.
 62. The electrochemical device according to claim 61, wherein said alloy has a nickel content of 50% by weight.
 63. The electrochemical device according to claim 51, wherein said ceramic portion has a particle size not higher than 50 nm.
 64. The electrochemical device according to claim 63, wherein said ceramic portion has a particle size of 1 to 25 nm.
 65. The electrochemical device according to claim 51, wherein said ceramic portion is doped ceria.
 66. The electrochemical device according to claim 65, wherein said ceramic portion is selected from gadolinia-doped ceria and samaria-doped ceria.
 67. The electrochemical device according to claim 51, wherein said anode comprises cerium oxide.
 68. The electrochemical device according to claim 47, comprising an anode containing nickel and an electrolyte membrane comprising a material of formula La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y)) wherein x and y are independently a value of 0.1 to 0.3, said material having a relative density of at least 90% and comprising LaSrGaO₄ in a percentage of 0.05 vol % to 10 vol %, said electrolyte membrane being in direct contact with at least said anode.
 69. The electrochemical device according, to claim 47, wherein said anode comprises a ceramic containing at least one of cobalt and iron, said ceramic being mixed with doped ceria.
 70. The electrochemical device according to claim 69, comprising a ratio of ceramic/doped ceria of 50:50 to 95:5.
 71. The electrochemical device according to claim 70, comprising a ratio of ceramic/doped ceria of 60:40 to 80:20.
 72. The electrochemical device according to claim 69, wherein said ceramic has a perovskite or a perovskite-related structure.
 73. The electrochemical device according to claim 69, wherein said ceramic contains cobalt and iron.
 74. The electrochemical device according to claim 69, wherein said ceramic is La_(0.6)Sr_(0.4)CO_(0.2)Fe_(0.08)O_(3−δ).
 75. The electrochemical device according to claim 47, wherein the cathode comprises a ceramic selected from: La_(1−e)Sr_(e)Mn_(f)O_(3−δ), wherein e and f are independently equal to a value of 0 to 1, and δ is from stoichiometry; and La_(1−c)Sr_(c)Co_(1−d)Fe_(d)O_(3−δ), wherein c and d are independently equal to a value of from 0 to 1, and δ is from stoichiometry.
 76. The electrochemical device according to claim 47, wherein the cathode comprises doped ceria.
 77. The electrochemical device according to claim 47, wherein the electrolyte membrane material of formula La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y)) has a perovskite structure.
 78. The electrochemical device according to claim 47, wherein the electrolyte membrane material is of formula La_(0.8)Sr_(0.2)Ga_(0.8)Mg_(0.2)O_(3−δ).
 79. The electrochemical device according to claim 47, wherein the electrolyte membrane material has a relative density of 95% to 99%.
 80. The electrochemical device according to claim 47, wherein LaSrGaO₄ is present in a percentage of 0.1 vol % to 6 vol %.
 81. The electrochemical device according to claim 47, wherein LaSrGaO₄ is in an amount increasing from the surface to the interior of the electrolyte membrane.
 82. The electrochemical device according to claim 81, wherein the amount of LaSrGaO₄ at the surface of the electrolyte membrane is substantially null.
 83. The electrochemical device according to claim 47, wherein the electrolyte membrane material of formula La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y)) is substantially free of LaSrGa₃O₇.
 84. A method for producing energy comprising the steps of: feeding at least one fuel into an anode side of a solid oxide fuel cell comprising an anode, a cathode and an electrolyte membrane disposed between said anode and said cathode, wherein said electrolyte membrane comprises a material of formula La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y)) wherein x and y are independently a value of 0.1 to 0.3, said material having a relative density of at least 90% and comprising LaSrGaO₄ in a percentage of 0.05 vol % to 10 vol %; feeding an oxidant into a cathode side of said solid oxide fuel cell; and oxidizing said at least one fuel in said solid oxide fuel cell, resulting in production of energy.
 85. The method according to claim 84, wherein the fuel is hydrogen an alcohol, methanol, ethanol, propanol, a hydrocarbon in gaseous form, methane, ethane, butene; carbon dioxide, carbon monoxide, natural gas, reformed natural gas, biogas, syngas and mixtures thereof, in the presence of water, steam fuel, or an hydrocarbon in liquid form, diesel, toluene, kerosene and jet fuels.
 86. The method according to claim 85, wherein the fuel is methane.
 87. The method according to claim 85, wherein the fuel is substantially dry.
 88. The method according to claim 87, wherein the fuel is substantially dry methane.
 89. The method according to claim 84, wherein the solid oxide fuel cell operates at a temperature of 400° C. to 800° C.
 90. The method according to claim 87, wherein the solid oxide fuel cell operates at a temperature of 500° C. to 700° C.
 91. A method for separating oxygen from a gas mixture, comprising the steps of: feeding the gas mixture into a cathode side of a gas separator comprising an anode, a cathode and an electrolyte membrane disposed between said anode and said cathode, wherein said electrolyte membrane comprises a material of formula La_(1−x)Sr_(x)Ga_(1−y)Mg_(y)O_(3−0.5(x+y)), wherein x and y are independently a value of 0.1. to 0.3, said material having a relative density of at least 90% and comprising LaSrGaO₄ in a percentage of 0.05 vol % to 10 vol %; applying an external potential difference between the cathode and the anode; dissociating the oxygen at the cathode to yield oxygen ions; diffusing the oxygen ions through the electrolyte membrane from the cathode to the anode; and converting the diffused oxygen ions to oxygen at the anode.
 92. The method according to claim 91, wherein the gas mixture is air. 